Abstract The objective of this work was to evaluate the mechanical performance of Z350 resin composite modified with Bombyx mori cocoons silk nanoparticles for dental applications. Four experimental groups were analyzed G0% = Filtek Z350 resin composite (control); G1% = Filtek Z350 with 1% of silk nanoparticles; G3% = Filtek Z350 with 3% of silk nanoparticles; G5% = Filtek Z350 with 5% of silk nanoparticles. It was employed scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, 3-point flexural strength test, Knoop hardness test, and surface roughness. From 3-point flexural strength tests the control group presented the best results G0% = 113.33 MPa (±23.73). The higher flexural modulus was shown by groups G3% = 29.150 GPa (±5.191) and G5% = 34.101 GPa (±7.940), which are statistically similar. The Knoop microhardness test has shown statistical difference only among the G3% group between the top 80.78 (± 3.00) and bottom 68.80 (±3.62) and no difference between the groups. The roughness test presented no statistical difference between the groups. The incorporation of silk nanoparticles reduced the flexural strength of Z350 resin composite. The surface roughness and microhardness tests showed no changes in any of the groups studied.

Resumo O objetivo deste trabalho foi avaliar o desempenho mecânico da resina composta Z350 modificada com nanopartículas de seda Bombyx mori cocoons para aplicações odontológicas. Quatro grupos experimentais foram analisados: G0%) Resina Z350 apenas (grupo controle); G1%) Reforço com 1% de nanopartículas de seda; G3%) Reforço com 3% de nanopartículas de seda; e G5%) Reforço com 5% de nanopartículas de seda. Foi empregado microscopia eletrônica de varredura, espectroscopia de energia dispersiva de raios X, difração de raios X, teste de resistência à flexão de 3 pontos, teste de dureza Knoop e rugosidade superficial. Nos testes de resistência à flexão de 3 pontos o grupo controle apresentou melhores resultados G0% = 0.113 GPa (±0.024). O maior módulo de flexão foi demonstrado pelos grupos G3% = 29.151GPa (±5.191) e G5% = 34.102 GPa (±7.94), que são estatisticamente semelhantes. O teste de microdureza Knoop mostrou diferença estatística apenas entre o grupo G3% entre os 80.78 superiores (± 3.00) e os 68.80 inferiores (±3.62). Não há diferença entre os grupos. O teste de rugosidade não apresentou diferença estatística entre os grupos. A incorporação de nanopartículas de seda reduziu a resistência à flexão da resina composta Z350. Os testes de rugosidade superficial e microdureza não apresentaram alterações em nenhum dos grupos estudados.

Resumo Este estudo apresenta a síntese de cimentos de ionômero de vidro (GIC) modificados com nanopartículas de fosfato de cálcio (nCaP). Os nCaP / GIC foram submetidos a ensaios mecânicos de compressão e tração diametral. Os biocompósitos foram caracterizados por microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva de raios-X (EDX), difração de raios-X (XRD) e espectroscopia de infravermelho com transformada de Fourier (FTIR). Os testes de citotoxicidade e viabilidade celular foram realizados em células-tronco mesenquimais da medula óssea humana usando um ensaio de 3- (4,5-dimetiltiazol-2-il) 2,5-difeniltetrazólio-brometo e ensaios LIVE / DEAD. Diferenças estatisticamente significativas foram observadas para as propriedades mecânicas (Kruskal-Wallis, p <0,001), nCaP / GIC apresentou maior resistência à compressão e tração diametral. As análises de SEM revelaram uma distribuição uniforme de nCaP na matriz do ionômero. Os resultados de EDX e DRX indicaram fases de hidroxiapatita e β-trifosfato de cálcio. Os espectros de FTIR revelaram a banda assimétrica de ν3PO4 3- entre 1100-1030cm-1 e a banda de vibração associada a ν1PO4 3- em 963cm-1 associada a nCaP. O nCaP / GIC apresentou resposta adequada à viabilidade celular e comportamento não citotóxico. Portanto, o novo compósito nCaP / GIC apresentou ótimas propriedades mecânicas, comportamento não citotóxico e resposta adequada à viabilidade celular com promissoras aplicações odontológicas.

Abstract This study showed the synthesis of Glass ionomer cements (GIC) modified with calcium phosphate nanoparticles (nCaP). The nCaP/GIC were submitted to mechanical compression and diametral tensile tests. The biocomposite were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR). Cytotoxicity and cell viability tests were performed on the human bone marrow mesenchymal stem cells using a 3-(4,5-dimethylthiazol-2yl)2,5-diphenyl- tetrazolium-bromide assay and LIVE/DEAD assays. Statistically significant differences were observed for mechanical properties (Kruskal-Wallis, p<0.001), nCaP/GIC showed higher resistance to compression and diametral traction. The SEM analyses revealed a uniform distribution nCaP in the ionomer matrix. The EDX and XRD results indicated that hydroxyapatite and calcium β-triphosphate phases. The FTIR spectra revealed the asymmetric band of ν3PO43- between 1100-1030cm-1 and the vibration band associated with ν1PO43- in 963cm-1 associated with nCaP. The nCaP/GIC presented response to adequate cell viability and non-cytotoxic behavior. Therefore, the new nCaP/GIC composite showed great mechanical properties, non-cytotoxic behavior, and adequate response to cell viability with promising dental applications.

Abstract Dental alloys are widely used in fabrication of removable partial dentures, particularly as a dental framework. The present study aimed at studying the effect of the commercial mouthwashes on the corrosion behavior of the Co−Cr dental casting alloy. Corrosion behavior was investigated in alcohol-free and alcohol-containing mouthwashes added to artificial saliva solutions at room temperature by electrochemical tests recorded the open circuit potential (OCP) and current density, after the surface analysis of the samples was performed. During the early 250s, the OCP values showed significant changes, with the exception of one test group containing alcohol, where potential decreased continuously during the test, which also recorded the highest current density, different from the other groups. It was observed that the presence of alcohol increased the current density and the corrosion process in this alloy and the mouthwashes had more aggressive action in specimens submitted to solutions with alcohol in the composition.

Objective The aim of this study was to evaluate the electrochemical behavior of a cobalt-chromium (Co-Cr) dental alloy after immersion in denture cleansers. Method: Twenty-four specimens (Ø13x2mm) of Co-Cr were produced and divided into three groups (n=8) according to their experimental condition. The group 1 (control group) was composed only of distilled water, group 2 received a hygienic tablet (Corega Tabs™) at the moment that electrochemical test started, while the group 3 received the hygienic tablet (Corega Tabs™) 1h after immersion. The electrochemical tests recorded the open circuit potential (OCP) and current density (icorr). The surfaces of specimens were examined using a SEM. Data were statistically analyzed using analysis of variance (ANOVA) and Duncan test’ multiple comparisons post hoc analysis (α=0.05). Results: The values of OCP and icorr revealed statistically differences between the groups. The highest results were recorded for group 2 (-26.87±48.48mV; 0.29±0.22μA), which were similar to group 3 (-47.37±35.36mV; 0.26±0.10μA), and these values were difference to group 1 (-314.87±24.22mV; 0.50±0.17μA). SEM image show high corrosion with Corega Tabs™. Conclusion: The immersion in denture cleanser solution was not detrimental to the Co-Cr dental alloy and presented a lower tendency to corrosion process development than the control group.

Abstract The moral values of good living Sumak Kawsay related to the respect for the Quichua language and culture represent a fundamental tool in Ecuadorian society and in school context. Therefore, the main objective of this study seeks to learn more about common and differentiating elements from the opinions of teachers and from the contents of textbooks in Ecuador. The research project was carried out in an indigenous community with 60 indigenous teachers of the rural school Mushauk Rimak located in San Lucas. A qualitative method was applied to the analysis of semi-open interviews in Spanish with the participating teachers. The results indicate that San Lucas teachers impart to students the values of respect for language and culture associated with the moral values of Sumak Kawsay. This aspect of the program is also reflected in the teaching materials in Quichua, component of the implementation of bilingual-intercultural education in the indigenous communities at the national level. The conclusion of the study points to the value of Sumak Kawsay as reflected in the content of textbooks and the efforts of teachers to revitalize the Quichua language and transmit the language to students despite the possibility that the bilingual program does not enjoy acceptance by all parents in this locality.

Resumen Los valores morales de buen vivir Sumak Kawsay relacionado con el respeto por la lengua y cultura quichua representan una herramienta fundamental en la sociedad ecuatoriana y en el contexto escolar. Consecuentemente con esta idea, el objetivo principal de este trabajo es averiguar los elementos comunes y diferenciadores entre las opiniones del profesorado indígena y los contenidos de los libros de texto de diferentes materias escolares de Ecuador. La investigación se desarrolló en un contexto indígena ecuatoriano con 60 docentes indígenas de la escuela rural Mushuk Rimak ubicada en la parroquia de San Lucas. Se utilizó la investigación cualitativa mediante las entrevistas semiabiertas en lengua castellana, que se realizaron a todos los docentes participantes. Los resultados indican que, en la comunidad indígena de San Lucas, los docentes transmiten al alumnado el valor del respeto por la lengua y cultura quichua vinculado con los valores morales del Sumak Kawsay. Este aspecto está reflejado también en los materiales educativos en quichua gracias a la política de implementación de educación bilingüe intercultural en los pueblos indígenas a nivel nacional en Ecuador. Las conclusiones destacan el valor del Sumak Kawsay en los libros de textos y la labor de los docentes de rescatar el idioma quichua y transmitirlo al alumnado a pesar que la aceptación del programa bilingüe no es unánime entre los padres y las madres de familia de esta localidad.

Resumo Introdução O uso de drogas entre adolescentes está aumentando, e o hábito vem se enraizando cada vez mais precocemente. Objetivo Investigar a associação do uso de drogas lícitas e ilícitas, sexo e condição socioeconômica entre adolescentes de 12 anos. Método Estudo transversal foi realizado em amostra representativa de adolescentes matriculados em escolas públicas e privadas da área urbana de Diamantina, Minas Gerais. Dados foram coletados por meio de questionários autoaplicados. O consumo de drogas foi investigado utilizando o instrumento ASSIST (Teste para Triagem do Envolvimento com Álcool, Cigarro e Outras Substâncias). Para investigar a condição socioeconômica, foram utilizados os indicadores: tipo de escola, renda familiar e escolaridade materna. As associações foram testadas pelos testes do Qui-quadrado de Pearson e Exato de Fisher (p < 0,05). Resultados A prevalência do consumo de álcool foi de 45,6% (260/588); uso de maconha, de 1,5% (9/588); de cocaína, 0,3% (2/588); e de inalantes, 1,7% (10/588). Sexo masculino esteve associado estatisticamente com consumo de maconha (p = 0,018) e de álcool (p = 0,012), mas não com uso de inalantes (p = 0,536). Na amostra estudada, não foi observada associação estatisticamente significativa entre o consumo de drogas ilícitas e os indicadores socioeconômicos. O consumo de álcool esteve associado ao uso de maconha p = 0,013 [OR:9,814 (1,220-78,984)]. Conclusão O consumo de álcool e o uso de maconha estiveram estatisticamente associados com o sexo masculino, mas não com os indicadores socioeconômicos.

Abstract Background Drug use among adolescents is on the rise, and the habit has been taking root at an increasingly early age. Objective Investigate the correlation between use of licit and illicit drugs, sex, and socioeconomic conditions among 12-year-old adolescents. Method Cross sectional study conducted with a representative sample of adolescents enrolled in public and private schools in the urban area of Diamantina, Minas Gerais state, Brazil. Data were collected through self-administered questionnaires. Consumption of drugs was investigated using the Alcohol, Smoking and Substance Involvement Screening Test (ASSIST) instrument. School type, family income, and maternal education were used to investigate socioeconomic condition. Associations were tested using the Pearson’s chi-square and Fisher's exact tests (p < 0.05). Results The following drug consumption prevalence values were found: alcohol, 45.6% (260/588); marijuana, 1.5% (9/588), cocaine, 0.3% (2/588); inhalants, 1.7% (10/588). The male gender was statistically associated with consumption of marijuana (p = 0.018) and alcohol (p = 0.012), but not with use of inhalants (p = 0.536). No statistically significant correlation was observed between consumption of licit and illicit drugs and the socioeconomic indicators adopted. Alcohol consumption was associated with use of marijuana (p = 0.013) [OR:9.814 (1.220 to 78.984)]. Conclusion Alcohol consumption and use of marijuana were statistically associated with the male gender, but not with socioeconomic indicators.

Abstract Literature has reported positive results regarding the use of lasers in the control of erosive lesions; however, evaluating whether they are effective in the control of the progression of erosive/abrasive lesions is important. Objectives This study aimed to evaluate the effect of the Er:YAG laser irradiation in controlling the progression of erosion associated with abrasive lesions in enamel. Material and methods Bovine incisors were sectioned, flattened and polished. Forty-eight enamel slabs were subjected to treatment in an intraoral phase. Twelve volunteers used an intraoral appliance containing one slab that was irradiated with an Er:YAG laser (5.2 J/cm2, 85 mJ, 2 Hz) and another non-irradiated slab on each side of the appliance, during one phase of 5 d, under a split-mouth design. Devices were subjected to erosive challenges (1% citric acid, 5 min, 3 times a day) and abrasive challenges one h after (brushing force of 1.5 N for 15 s) randomly and independently on each side of the device. Measurements of enamel loss were performed via 3D optical profilometry (μm). We analyzed data using the Kruskal-Wallis and Mann-Whitney tests and morphological characteristics via scanning electron microscopy. Results Following erosive and abrasive challenges, the group that was irradiated with the Er:YAG laser presented less loss of structure than the non-irradiated group. The group that underwent erosion and irradiation did not exhibit a significant difference from the non-irradiated group. Conclusion Irradiation with the Er:YAG laser did not control the loss of structure of enamel subjected to erosion but did control abrasion after erosion.

RESUMO OBJETIVO: o objetivo deste estudo foi avaliar in vitro a influência do laser de CO2 sobre a resistência ao cisalhamento da colagem (RCC) no esmalte dentário, usando diferentes tipos de braquetes cerâmicos. MÉTODOS: no total, 60 superfícies de esmalte de incisivos bovinos foram obtidas e aleatoriamente divididas em dois grupos, de acordo com o braquete cerâmico utilizado: Allure (A) e Transcend (T). Cada grupo foi dividido em dois subgrupos (n = 15): L, laser (10W, 3s); C, sem laser, ou controle. Vinte e quatro horas após a colagem dos braquetes com o sistema Transbond XT, foi realizado o teste de resistência ao cisalhamento, com velocidade de 0,5 mm/min, em máquina universal de ensaios mecânicos. Após a descolagem, o Índice de Remanescente de Adesivo (IRA) foi avaliado com aumento de 10X e comparado entre os grupos. Os dados foram analisados pelo ANOVA one-way, testes de Tukey’s, Mann-Whitney’s e Kruskal-Wallis (α = 0,05). RESULTADOS: as médias da RCC em MPa foram: AL = 0,88 ± 0,84; AC = 12,22 ± 3,45; TL = 12,10 ± 5,11; TC = 17,71 ± 6,16. A análise do IRA mostrou que 73% dos corpos de prova apresentaram todo o compósito remanescente aderido à superfície do esmalte (escore 3). O grupo TC apresentou valor significativamente maior de RCC do que os outros grupos. Os corpos de prova dos grupos com laser obtiveram valores adesivos significativamente menores do que os corpos de prova dos grupos sem laser, com ambos os tipos de braquetes. CONCLUSÃO: a irradiação com laser de CO2 diminuiu os valores de RCC dos braquetes policristalinos testados, principalmente do Allure.

ABSTRACT OBJECTIVE: The aim of this study was to assess in vitro the influence of the CO2 laser and of the type of ceramic bracket on the shear bond strength (SBS) to enamel. METHODS: A total of 60 enamel test surfaces were obtained from bovine incisors and randomly assigned to two groups, according to the ceramic bracket used: Allure (A); Transcend (T). Each group was divided into 2 subgroups (n = 15): L, laser (10W, 3s); C, no laser, or control. Twenty-four hours after the bonding protocol using Transbond XT, SBS was tested at a crosshead speed of 0.5 mm/min in a universal testing machine. After debonding, the Adhesive Remnant Index (ARI) was evaluated at 10 x magnification and compared among the groups. Data were analyzed by one-way ANOVA, Tukey’s, Mann-Whitney’s and Kruskal-Wallis tests (α = 0.05). RESULTS: Mean SBS in MPa were: AL = 0.88 ± 0.84; AC = 12.22 ± 3.45; TL = 12.10 ± 5.11; TC = 17.71 ± 6.16. ARI analysis showed that 73% of the specimens presented the entire adhesive remaining on the tooth surfaces (score 3). TC group presented significantly higher SBS than the other groups. The lased specimens showed significantly lower bond strength than the non-lased groups for both tested brackets. CONCLUSION: CO2 laser irradiation decreased SBS values of the polycrystalline ceramic brackets, mainly Allure.

Resumo Este estudo avaliou o efeito dos inibidores de metaloproteinase, clorexidina 2% e fluoreto de sódio (5000 ppm), na resistência de união entre a dentina irradiada por laser Er:YAG e a resina composta após a degradação química da interface de união. A superfície oclusal de quarenta molares humanos hígidos (n=10) foi removida expondo uma superfície de dentina, que foi polida, irradiada com laser Er:YAG, condicionada com ácido e seca. Vinte espécimes foram re-umedecidos com clorexidina 2% (Grupo controle) e 20 com fluoreto de sódio (5000 ppm). O sistema adesivo foi aplicado e um platô de resina composta fotopolimerizável de 4 mm de altura foi construído. Palitos de resina-dentina foram obtidos com secção transversal retangular (0,8-1 mm2). Eles foram armazenados em água (24 h a 37 ?#61616;C) ou submetidos a degradação química. Para a degradação química, foram imersos em solução aquosa de hipoclorito de sódio a 10% durante 5 horas e lavados em água durante 1 h. Os palitos foram submetidos ao teste de microtração em uma máquina de ensaios mecânicos a 0,5 mm/min até a fratura. O padrão de fratura foi analisado em MEV. Os valores de resistência de união foram calculados em MPa e submetidos à análise de variância ANOVA (α=0,05). A análise de variância mostrou que os fatores inibidor de metaloproteinases e degradação (p=0,214 e p=0,093, respectivamente), e a interação entre os fatores não foram estatisticamente significantes (p=0,143). A predominância de falha mista foi detectada para todos os grupos. Em conclusão, a clorexidina a 2% e fluoreto de sódio (ppm 5000) apresentaram resistência de união entre dentina irradiada e resina composta semelhante antes e após a degradação química.

Abstract This study evaluated the effect of matrix metalloproteinase (MMP) inhibitors - 2% (CHX) and sodium fluoride (NaF) (5000 ppm) - on microtensile bond strength (μTBS) of composite resin to Er:YAG laser-irradiated dentin after chemical degradation of the bond interface. The occlusal surface of forty sound human molars was removed exposing the dentin surface (n=10), which was polished, irradiated with Er:YAG laser, acid etched and dried. Twenty specimens were rewetted with 2% CHX (control group) and 20 were rewetted with NaF (5000 ppm). The adhesive system was applied and a 4-mm-high plateau of light-cured composite resin was built up. Resin-dentin sticks were obtained with a rectangular cross-sectional area (0.8-1 mm2) and were either stored in water at 37 ?#61616;C for 24 h or submitted to chemical degradation. For chemical degradation, they were immersed in 10% NaOCl aqueous solution for 5 h and rinsed in water for 1 h. The sticks were submitted to microtensile test in a mechanical testing machine at 0.5 mm/min until failure. Fracture pattern was analyzed using SEM. μTBS values were calculated in MPa and submitted to analysis of variance ANOVA (α=0.05). The variance analysis showed that the 'MMP inhibitor' and 'degradation' factors (p=0.214 and p=0.093, respectively) and interaction between the factors were not statistically significant (p=0.143). Mixed failure predominated in all groups. In conclusion, the 2% CHX and NaF 5000 ppm presented similar μTBS of composite resin to laser-irradiated dentin before and after chemical degradation

Resumo Selantes dentários são importantes para a prevenção de lesões de cárie desde que tenham boa resistência ao cisalhamento. O objetivo deste trabalho foi avaliar a resistência ao cisalhamento (SBS), de dois selantes em esmalte contaminado e não contaminado com saliva, com e sem uma camada adesiva intermediária sob o selante. Noventa superfícies de esmalte de terceiros molares humanos foram planificadas e divididas aleatoriamente em 6 grupos (n=15): F (controle): selante Fluroshield(tm); EWB (controle): Embrace(tm) WetBond(tm); SB/F: sistema adesivo Single Bond + F; SB/EWB, s-SB/F and s-SB/EWB. Nos grupos s-SB/F e s-SB/EWB, a contaminação do esmalte condicionado foi obtida com 0,01 mL de saliva humana fresca durante 20 s. Cilindros de selante foram colocados sobre a superfície do esmalte com e sem uma camada de sistema adesivo intermediária. Os ensaios de cisalhamento foram realizados utilizando uma máquina universal de ensaios (0,5 mm/min). Os dados foram analisados estatisticamente pelo teste de Kruskal-Wallis e Mann-Whitney (?#61537;=0,05). F apresentou valores médios de SBS maiores do que EWB em todas as condições experimentais. O menor valor médio de SBS foi obtido pelo EWB em esmalte contaminado (p<0,05). Em conclusão, uma camada de sistema de adesivo deve ser utilizada antes da colocação do selante, tanto em superfície seca quanto contaminada por saliva. F teve o melhor desempenho em todas as condições experimentais. O selante EWB apresentou resultados insatisfatórios, porém o uso de uma camada adesiva abaixo do selante aumentou sua SBS, mesmo após a contaminação salivar.

Abstract Dental sealants are important for prevention of carious lesions, if they have good shear strength. The aim of this study was to evaluate the shear bond strength (SBS) of two sealants to saliva-contaminated and non-contaminated enamel with and without an intermediate adhesive layer underneath the sealant. Ninety flat enamel surfaces from human third molars were randomly assigned to 6 groups (n=15): F (control): Fluroshield(tm) sealant; EWB (control): Embrace(tm) WetBond(tm); SB/F: Single Bond adhesive system + F; SB/EWB, s-SB/F and s-SB/EWB. In the s-SB/F and s-SB/EWB groups, the acid-etched enamel was contaminated with 0.01 mL of fresh human saliva for 20 s. Sealant cylinders were bonded to enamel surface with and without an intermediate adhesive system layer. The shear tests were performed using a universal testing machine (0.5 mm/min). Data were analyzed statistically by Kruskal-Wallis and Mann-Whitney tests (α=0.05). F presented higher mean SBS than EWB in all experimental conditions. The lowest SBS mean was obtained for EWB on contaminated enamel (p<0.05). In conclusion, an adhesive system layer should be used prior to sealant placement, in both dry and saliva-contaminated enamel. F had the best performance in all experimental conditions. EWB sealant showed very low results, but an adhesive layer underneath the sealant increased its SBS even after salivary contamination.

Resumo Esse estudo avaliou o feito combinado do verniz fluoretado ao laser de Er:YAG na permeabilidade da dentina radicular erodida. Fragmentos de dentina radicular bovina, foram submetidos a um desafio erosivo inicial com ácido cítrico, que foi seguido por um período de remineralização. Posteriormente, os espécimes foram divididos em relação aos tratamentos: verniz (fluoretado e não fluoretado) e subdivididos de acordo com a irradiação: laser de Er:YAG (100 mJ, 3 Hz, 12.8 J/cm2 por pulso, sem contato e modo não focado) e não irradiado. Após um período de lead in, 7 voluntários utilizaram um dispositivo palatino contendo 4 espécimes que foram submetidos a desafios erosivos. Na primeira fase do experimento, 4 voluntários utilizaram dispositivos com fragmentos tratados com verniz fluoretado e verniz fluoretado+laser de Er:YAG e 3 voluntários utilizaram espécimes tratados com verniz não fluoretado e verniz não fluoretado+laser de Er:YAG. Depois de um período de wash-out, os voluntários foram cruzados em relação aos tratamentos, caracterizando um experimento cross-over 2x2. Ao final de cada fase experimental, a variável resposta quantitativa foi obtida através da análise de permeabilidade e a qualitativa por microscopia eletrônica de varredura (MEV). A ANOVA dois critérios e teste de Tukey-Kramer revelou que as amostras tratadas com verniz fluoretado+laser de Er:YAG mostraram menor permeabilidade e uma diferença significativa foi encontrada entre este grupo, quando comparado aos demais grupos. Quando o verniz (fluoretado/não fluoretado) foram aplicados na ausência do laser de Er:YAG maiores valores de permeabilidade foram encontrados quando comparados com os grupos irradiados com o laser. A MEV demostrou túbulos dentinários parcialmente ou completamente ocluídos quando as amostras foram tratadas com verniz fluoretado+laser de Er: YAG. Pode-se concluir que o laser de Er:YAG foi capaz de controlar a permeabilidade da dentina radicular erodida e essa ação é aumentada quando o laser está associado ao verniz fluoretado.

This study evaluated the combined effect of fluoride varnish and Er:YAG laser on the permeability of eroded bovine root dentin. After initial erosive challenge followed by a remineralization period, the specimens were divided in two groups according to the treatment - fluoride varnish and non-fluoride varnish - and were subdivided according to the irradiation protocol: Er:YAG laser (100 mJ, 3 Hz, 12.8 J/cm2per pulse, non-contact and defocus mode) and non-irradiated. After a lead-in period, 7 volunteers wore a palatal device containing 4 specimens that were subjected to erosive challenges. At the first experimental phase, 4 volunteers used specimens treated with fluoride varnish and fluoride varnish+Er:YAG laser and 3 volunteers used specimens treated with non-fluoride varnish and non-fluoride varnish+Er:YAG laser. After a washout period, volunteers were crossed to treatments, characterizing a 2x2 crossover experiment. At the end of the experimental phase, the quantitative response variable was obtained by permeability analysis and the qualitative response by scanning electron microscopy (SEM). Two-way ANOVA and Tukey-Kramer's test revealed that specimens treated with fluoride varnish+Er:YAG laser showed the lowest permeability and a significant difference was found between this group and the others. When varnish (fluoride/non-fluoride) was applied in the absence of Er:YAG laser, higher permeability was found when compared to the laser-treated groups. SEM evaluations showed partially or completely obliterated dentinal tubules when specimens were treated with fluoride varnish+Er:YAG laser. It may be concluded that Er:YAG laser was able to control the permeability of eroded root dentin and the combination with fluoride varnish increased laser action.

AbstractThe aim of this study was to manufacture a new zirconia implant (Y-TZP) and to evaluate the fracture strength and stresses generated after cyclic loading compared to titanium implants. Thirty-three zirconia and titanium implants were fabricated. The stress generated around the implants was observed by photoelastic analysis. The implants were then separated into groups (n = 10): Control (no treatment), mechanical fatigue and thermomechanical fatigue. All groups were submitted to a single cantilever flexure test to measure the material fracture strength. The results (2-way ANOVA, Bonferroni test, p <.05) showed no statistically significant difference in the stresses generated between the zirconia and titanium implants. Titanium implants showed higher fracture strength than the zirconia implants, a property that was not altered by fatigue applied. It was concluded that stress distribution was similar for Zr and Ti and mechanical and thermomechanical fatigue had no influence on the fracture strength of the implants tested.

AIM: To analyze the dental arches by occlusal radiographs for possible gender differentiation. METHODS: One hundred occlusal radiographic images were obtained. First, a median line and a line touching the vestibular portions of the projections of the maxillary central incisors were drawn. The intersection of these lines was called point I and from this point a line to the canine most vestibular portion was drawn, from the second premolar and second molar, from the left and right sides, in the maxillary and mandibular arches, thus obtaining the angle measurements. Line measurements relative to the width of the arches in three segments, canines, premolars and second molars were made. RESULTS: The analyses performed by t-test indicated that all linear values obtained were statistically different p<0.05, as may be seen in the values obtained from canine to canine, in which the female average was 3.48 cm 0.16 while the male average was 3.74 cm 0.21 and in respect to the angle measurements, only two angles have shown applicability in the definition of gender. CONCLUSIONS: Gender can be determined by analysis of occlusal radiographs with greater reliability when linear measurements are performed.

Objective: The present study evaluated the use of a reagent to stabilize the DNA extracted from human dental tissues stored under different temperature conditions and time intervals. Material and Methods: A total of 161 teeth were divided into two distinct groups: intact teeth and isolated dental pulp tissue. The samples were stored with or without the product at different time intervals and temperature. After storage, DNA extraction and genomic DNA quantification were performed using real-time PCR; the fragments of the 32 samples that represented each possible condition were analyzed to find the four pre-selected markers in STR analysis. Results: The results of the quantification showed values ranging from 0.01 to 10,246.88 ng/μL of DNA. The statistical difference in the quantity of DNA was observed when the factors related to the time and temperature of storage were analyzed. In relation to the use of the specific reagent, its use was relevant in the group of intact teeth when they were at room temperature for 30 and 180 days. The analysis of the fragments in the 32 selected samples was possible irrespective of the amount of DNA, confirming that the STR analysis using an automated method yields good results. Conclusions: The use of a specific reagent showed a significant difference in stabilizing DNA in samples of intact human teeth stored at room temperature for 30 and 180 days, while the results showed no justification for using the product under the other conditions tested.